标题: Nickel based oxide film formed in molten salts for efficient electrocatalytic oxygen evolution

作者: Liang, XX (Liang, Xin Xin); Weng, W (Weng, Wei); Gu, D (Gu, Dong); Xiao, W (Xiao, Wei)

来源出版物: JOURNAL OF MATERIALS CHEMISTRY A  : 7  : 17  : 10514-10522  DOI: 10.1039/c9ta00997c  出版年: MAY 7 2019  

摘要: Implementation of non-precious, active and durable catalysts towards the oxygen evolution reaction (OER) is a promising protocol addressing challenges in energy and environmental sustainability. Herein, a binderfree film composed of nickel ferrite is prepared by the anodic oxidation of a nickel alloy in molten salts. Merits of the electrochemical oxidation in molten salts are highlighted by the generation of the spinel NiFe2O4 film over the Ni-Fe-Cu substrate with full exposure of OER-active Fe species, absence of OERinert CuO species and good adhesion with the substrate. The prepared film electrode therefore exhibits higher electrocatalytic activity than the commercial IrO2/Ta2O5-Ti electrode towards the OER in an alkaline electrolyte. The overpotential to drive a current density of 10 mA cm-2 for the as-prepared electrode is only 326 mV, 27 mV less than that for the IrO2/Ta2O5-Ti electrode. Besides, the prepared nickel ferrite film also exhibits a low Tafel slope of 35.9 mV dec-1, an excellent turnover frequency (TOF) value of 0.85 s-1 at an overpotential of 300 mV and high stability after electrolysis at 50 mA cm-2 for 60 h in 1.0 M KOH. The present study highlights the potential for utilization of electrochemical oxidation of metallic substrates in molten salts for the fast preparation of high-quality oxide films with promising functionalities.

入藏号: WOS:000472183200038

语言: English

文献类型: Article

地址: [Liang, Xin Xin; Weng, Wei; Xiao, Wei] Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.

[Gu, Dong] Wuhan Univ, Inst Adv Studies, Wuhan 430072, Hubei, Peoples R China.

通讯作者地址: Xiao, W (通讯作者)Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.

电子邮件地址: gabrielxiao@whu.edu.cn


学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © www.402.com-永利总站网址是多少-77402
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893